ResinTech - Products

Cation Exchange Resins
Anion Exchange Resins
Mixed Bed Resins and Regenerated Products
Tribed Resins and Inert Media
Selective Ion Exchange Resin and Media
Activated Carbon

Click here for printable sheet.

CATION EXCHANGE RESINS
PRODUCT	TYPE	IONIC FORM	APPROX SHIP WT lbs/cu.ft.	SCREEN SIZE US mesh percent	WATER RETENTION percent	TOTAL CAPACITY meq/ml (kgr./cu.ft.)	MAX TEMP. Degrees F.	SWELLING percent	RECOMMENDED USES
CG8	Strong Acid Gel 8% DVB	Na	52	+16 <2 -50 <1	45- 49	1.95 (42.6)	280	Na to H 5- 9	Premium grade gel type strong acid cation resin suitable for softening, and demineralization, including mixed beds, dealkalization. Supplied in the hydrogen form as CG8-H. Available in black color for easy visual separation in mixed beds.
CG8- H	Strong Acid Gel 8% DVB	H	50	+16 <2 -50 <1	49- 54	1.85 (40.4)	265	—
CG8- C	Strong Acid Gel 8% DVB	Na	52	+16 <2 -45 <1	45- 49	1.95 (42.6)	280	Na to H 5- 9	CG8 with coarse bead size, intended for high flow rate applications and chemical process.
PRODUCT	TYPE	IONIC FORM	APPROX SHIP WT lbs/cu.ft.	SCREEN SIZE US mesh percent	WATER RETENTION percent	TOTAL CAPACITY meq/ml (kgr./cu.ft.)	MAX TEMP. Degrees F.	SWELLING percent	RECOMMENDED USES
CG8- F	Strong Acid Gel 8% DVB	Na	52	+16 <2 -50 <1	45- 49	1.95 (42.6)	280	Na to H 5- 9	CG8 with fine mesh size, intended for softening and iron removal.
CGS	Strong Acid Gel	Na	51	+16 <2 -50 <1	49- 53	1.9 (41.5)	280	Na to H 5- 12	Strong acid cation resin for use in domestic softening. Specially processed to be free of color, taste and odor.
CG10	Strong Acid Gel 10% DVB	Na	54	+16 <2 -50 <1	40- 45	2.2 (48.0)	280	Na to H 4- 8	Premium grade 10% DVB gel type strong acid cation resin. More resistant to oxidation than CG8. Excellent for high temperature applications, softening, deionization, and chemical processes. Particularly well suited for use in mixed beds. Also supplied in the hydrogen form as CG10-H. Available in black color for easy visual separation in mixed beds.
CG10- H	Strong Acid Gel 10% DVB	H	52	+16 <2 -50 <1	46- 53	2.1 (45.9)	265	—
PRODUCT	TYPE	IONIC FORM	APPROX SHIP WT lbs/cu.ft.	SCREEN SIZE US mesh percent	WATER RETENTION percent	TOTAL CAPACITY meq/ml (kgr./cu.ft.)	MAX TEMP. Degrees F.	SWELLING percent	RECOMMENDED USES
SACMP	Strong Acid Macroporousid	Na	50	+16 <2 -50 <1	47- 52	1.70 (37.2)	300	Ca or Na to H 4- 7	Macroporous structure and high DVB level gives this strong acid cation resin the best resistance to oxidative, thermal and osmotic stresses. Also supplied in the hydrogen form as SACMP-H.
SACMP-H	Strong Acid Macroporous	H	48	+16 <2 -50 <1	-50 56	51.6 (35.0)	300	—
WACG	Weak Acid Gel (Carboxylic)	H	47	+16 <2 -50 <1	42- 49	4.0 (87.4)	300	H to Na 100	This gel type weak acid cation resin has nearly 100% regeneration efficiency (Carboxylic) and an extraordinary total capacity, of over 85 kilograins/cu.ft. Useful in dealkalization and chemical processing applications. Also available in the sodium form for use in high TDS softening applications.
WACG- Na	Weak Acid Gel (Carboxylic)	Na	50	+16 <2 -50 <1	approx. 75	2.6 (43.7)	300	—
PRODUCT	TYPE	IONIC FORM	APPROX SHIP WT lbs/cu.ft.	SCREEN SIZE US mesh percent	WATER RETENTION percent	TOTAL CAPACITY meq/ml (kgr./cu.ft.)	MAX TEMP. Degrees F.	SWELLING percent	RECOMMENDED USES
WACMP	Weak Acid Macro (Carboxylic)	H	47	+16 <2 -50 <1	53- 58	3.8 (83.0)	250	H to Ca 27	High capacity macroporous weak acid cation resin with nearly 100% regeneration efficiency for dealkalization, deionization, etc., with improved physical stability. This resin is also available in the sodium form for use in high TDS softening applications.
WACMP- Na	Weak Acid Macro (Carboxylic)	Na	50	+16 <2 -50 <1	approx. 75	2.1 (45.9)	250	H to Na 80
WACMA	Weak Acid Macro (Methacrylic)	H	41	+16 <2 -50 <1	43- 53	3.9 (85.2)	250	—	Recommended for industrial and domestic softening. Has lower pH than WACMP and WACG.
WACMA- Na	Weak Acid Macro (Methacrylic)	Na	43	+16 <2 -50 <1	approx. 67	2.5 (54.6)	250	H to Na 75- 100	Product purification, buffering etc.

Click here for printable sheet.

ANION EXCHANGE RESINS
PRODUCT	TYPE	IONIC FORM	APPROX SHIP WT lbs/cu.ft.	SCREEN SIZE US mesh percent	WATER RETENTION percent	TOTAL CAPACITY meq/ml (kgr./cu.ft.)	MAX TEMP. Degrees F.	SWELLING percent	RECOMMENDED USES
SBG1	Strong Base Gel Type 1	Cl	44	+16 <2 -50 <1	43- 47	1.45 (31.7)	170	Cl to OH 18- 22	Standard gel Type 1 anion resin for use in condensate deionization and single use mixed beds. Has the highest total capacity of Type 1 gel anion resins. Superior physical strength and resistance to oxidation.
SBG1- OH	Strong Base Gel Type 1	OH	42	+16 <2 -50 <1	53- 60	1.2 (26.2)	140	—	Standard gel Type 1 anion resin supplied in the OH form for use in condensate deionization or single use mixed beds (radwaste), cartridges or single use separate beds (anion complexed metals).
SBG1P	Strong Base Gel Type 1 Porous	Cl	43	+16 <2 -50 <1	51- 57	1.25 (27.3)	170	Cl to OH 20- 27	Porous gel Type 1 anion resin, superior kinetics to SBG1, for use in deionization and mixed beds. Has the highest regenerable operating capacity of the Type 1 anion resins. Especially recommended for regenerable systems. Good resistance to organic fouling.
SBG1P- OH	Strong Base Gel Type 1 Porous	OH	41	+16 <2 -50 <1	65- 70	1.0 (21.9)	140	—
PRODUCT	TYPE	IONIC FORM	APPROX SHIP WT lbs/cu.ft.	SCREEN SIZE US mesh percent	WATER RETENTION percent	TOTAL CAPACITY meq/ml (kgr./cu.ft.)	MAX TEMP. Degrees F.	SWELLING percent	RECOMMENDED USES
SBG2	Strong Base Gel Type 2	Cl	44	+16 <2 -50 <1	38- 44	1.45 (31.7)	170	Cl to OH 10- 15	Standard gel Type 2 anion resin, featuring very high capacity and regeneration efficiency. Greater resistance to organics than Type 1 resins. Excellent for two bed service. Its good regeneration efficiency and high capacity can help minimize caustic consumption and save on operating costs.
SBG2- OH	Strong Base Gel Type 2	OH	42	+16 <2 -50 <1	43- 50	1.3 (28.4)	95	—
SBMP1	Strong Base Type 1 Macro	Cl	42	+16 <2 -50 <1	50- 60	1.15 (25.1)	170	Cl to OH 15- 20	Type 1 macroporous anion resin featuring high exchange capacity, porous gel matrix and superior elution of large organic molecules. Also offered in hydroxide form for immediate use.
SBMP1- OH	Strong Base Type 1 Macro	OH	40	+16 <2 -50 <1	64- 73	.95 (20.8)	140	—
PRODUCT	TYPE	IONIC FORM	APPROX SHIP WT lbs/cu.ft.	SCREEN SIZE US mesh percent	WATER RETENTION percent	TOTAL CAPACITY meq/ml (kgr./cu.ft.)	MAX TEMP. Degrees F.	SWELLING percent	RECOMMENDED USES
SBMP2	Strong Base Type 2 Macro	Cl	43	+16 <2 -50 <1	52- 58	1.2 (26.2)	170	Cl to OH 10- 15	Type 2 macroporous anion resin featuring high exchange capacity and superior elution of large organic molecules. Suitable for high salt content waters. Also offered in hydroxide form for immediate use.
SBMP2- OH	Strong Base Type 2 Macro	OH	41	+16 <2 -50 <1	62- 71	1.0 (21.9)	140	—
SBACR1	Strong Base Gel (Acrylic)	Cl	45	+16 <2 -50 <1	57- 62	1.2 (26.2)	95	Cl to OH 10- 15	Acrylic structure allows operating capacity and fouling resistance in applications with a high level of organics. This resin should not be used when service water temp exceeds 85 degrees F.
PRODUCT	TYPE	IONIC FORM	APPROX SHIP WT lbs/cu.ft.	SCREEN SIZE US mesh percent	WATER RETENTION percent	TOTAL CAPACITY meq/ml (kgr./cu.ft.)	MAX TEMP. Degrees F.	SWELLING percent	RECOMMENDED USES
SBACR2	Strong Base Gel (Acrylic)	Cl FB	43	+16 <2 -50 <1	57- 63	1.4 (30.6)	95	—	Acrylic resin containing a mixture of strongly basic and weakly basic exchange groups. High total capacity and resistance to organic fouling.
WBG30	Weak Base (Epoxy Polyamine)	CI FB	38	+16 <2 -50 <1	52- 62	3.0 (65.6)	110	FB to Cl 5	High capacity granular intermediate base resin for use in applications requiring extremely high throughput capacity or nearly 100 percent regeneration efficiency.
WBMP	Weak Base Macroporous	Free Base	40	+16 <2 -50 <1	48- 54	1.6 (35.0)	212	FB to Cl 10- 15	Macroporous weakly basic anion resin, with excellent physical strength and high throughput capacity. Nearly 100 percent regeneration efficiency and high resistance to organic fouling.
WBACR1	Weak Base (Acrylic)	Free Base	44	+16 <2 -50 <1	60- 65	1.7 (37.2)	250	FB to Cl 10- 15	Weakly basic acrylic resin with high total capacity, throughput capacity and regeneration efficiency. Organic substances sorbed during service are easily removed during regeneration.

Click here for printable sheet.

MIXED BED RESINS AND REGENERATED PRODUCTS
PRODUCT	TYPE	IONIC FORM	APPROX SHIP WT lbs/cu.ft.	SCREEN SIZE US mesh percent	WATER RETENTION percent	TOTAL CAPACITY meq/ml (kgr./cu.ft.)	MAX TEMP. Degrees F.	SWELLING percent	RECOMMENDED USES
CG8- H	Strong Acid Gel 8% DVB	H	50	+16 <2 -50 <1	49- 54	1.85 (40.4)	265	Na to H 5- 9	CG8 cation resin with high conversion to the hydrogen form, specially processed to reduce TOC throw.
CG10- H	Strong Acid Gel 10% DVB	H	52	+16 <2 -50 <1	46- 53	2.1 (45.9)	265	Na to H 5- 9	CG10 cation resin, with high conversion to the hydrogen form, specially processed to reduce TOC throw.
SBG1- OH	Strong Base Gel Type 1	OH	41	+16 <2 -50 <1	53- 60	1.2 (26.2)	140	Cl to OH 18- 22	Standard Type 1 anion resin with high degree of conversion to the hydroxide form, specially processed to reduce TOC throw.
PRODUCT	TYPE	IONIC FORM	APPROX SHIP WT lbs/cu.ft.	SCREEN SIZE US mesh percent	WATER RETENTION percent	TOTAL CAPACITY meq/ml (kgr./cu.ft.)	MAX TEMP. Degrees F.	SWELLING percent	RECOMMENDED USES
SBG1P- OH	Strong Base Gel Porous	OH	40	+16 <2 -50 <1	65- 70	1.0 (21.9)	140	Cl to OH 20- 27	Type 1 porous anion resin with high degree of conversion to the hydroxide form, specially processed to reduce TOC throw.
SBG2- OH (NG only)	Strong Base Gel Type 2	OH	43	+16 <2 -50 <1	43- 50	1.3 (28.4)	95	Cl to OH 10- 15	Type 2 anion resin with high degree of conversion to the hydroxide form, specially processed to reduce amine odor and retain a light amber color throughout its life.
SBMP1- OH	Strong Base Type 1 Macro	OH	40	+16 <2 -50 <1	64- 73	.95 (20.8)	140	Cl to OH 15- 20	Type 1 macroporous resin with high degree of conversion to the hydroxide form, specially processed to reduce TOC throw.
PRODUCT	TYPE	IONIC FORM	APPROX SHIP WT lbs/cu.ft.	SCREEN SIZE US mesh percent	WATER RETENTION percent	TOTAL CAPACITY meq/ml (kgr./cu.ft.)	MAX TEMP. Degrees F.	SWELLING percent	RECOMMENDED USES
MBD- 10	Strong Acid Gel Strong Base Gel (Type 1)	H/ OH	43	+16 <2 -50 <1	60 max	.68 (15)	140	Na/Cl to H/OH 15- 17	Mixed bed of highly regenerated hydrogen form cation and hydroxide form standard Type 1anion resin. Low TOC throw. High capacity is particularly useful for disposable cartridges and single use applications.
MBD- 12 (NG only)	Strong Acid Gel Strong Base Gel (Type 1 Porous)	H/OH	43	+16 <2 -50 <1	60 max	.60 (13)	140	Na/Cl to H/OH 18- 20	Mixed bed resin that changes color as its exhausts. Cation resin component is dyed. Great for cartridge applications where visual determination of exhaustion is needed.
MBD- 15	Strong Acid Gel Strong Base Gel (Type 1 Porous)	H/OH	43	+16 <2 -50 <1	60 max	.60 (13)	140	Na/Cl to H/OH 18- 20	Mixed bed of highly regenerated hydrogen form and hydroxide form porous Type 1 anion resin. Specially processed to minimize TOC throw. Best choice for regenerable applications and ultrapure water.
PRODUCT	TYPE	IONIC FORM	APPROX SHIP WT lbs/cu.ft.	SCREEN SIZE US mesh percent	WATER RETENTION percent	TOTAL CAPACITY meq/ml (kgr./cu.ft.)	MAX TEMP. Degrees F.	SWELLING percent	RECOMMENDED USES
MBD- 16	Strong Acid Gel Strong Base Gel (Type 1 Porous)	H/OH	43	+16 <2 -50 <1	60 max	.60 (13)	140	Na/Cl to H/OH 18- 20	Mixed bed of highly regenerated hydrogen form 10 percent DVB cation and hydroxide form porous Type 1 anion resin. Specially processed to minimize TOC throw. Best choice for regenerable applications. Gives great backwash separation.
MBD- 20 (NG only)	Strong Acid Gel Strong Base Gel (Type 2)	H/OH	43	+16 <2 -50 <1	60 max	.80 (17.4)	95	Na/Cl to H/OH 9- 11	Mixed bed of highly regenerated hydrogen form cation and hydroxide form Type 2 anion resin. Low amine throw. Very high operating capacity.
MBD- 30 (NG only)	Strong Acid Gel Strong Base Gel (Type 1)	H/OH	43	+16 <2 -50 <1	60 max	.60 (13)	140	Na/Cl to H/OH 18- 20	Mixed bed resin that changes color as it exhausts. Anion resin component is dyed. Great for cartridge applications where visual determination of exhaustion is needed.
*NOTE: Nuclear grade products are designated by NG suffix, semiconductor grade products by SC suffix and Low TOC products by SC- LTOC suffix. All nuclear grade mixed beds are tested to 15 megohm resistivity. All semiconductor grade mixed beds are tested to 18 megohm resistivity. All products available as nuclear grade, semiconductor grade or low TOC grade unless otherwise indicated.

Click here for printable sheet.

TRIBED RESINS
PRODUCT	TYPE	IONIC FORM	APPROX SHIP WT lbs/cu.ft.	SCREEN SIZE US mesh percent	WATER RETENTION percent	TOTAL CAPACITY meq/ml (kgr./cu.ft.)